品名规格
PE燃气管材规格 单位：mm
|
公称外径 |
压力等级 |
|||
|
SDR17.6 |
SDR11 |
|||
|
公称壁厚(mm) |
公称壁厚(mm) |
|||
|
20 |
2.3 |
3.0 |
||
|
25 |
2.3 |
3.0 |
||
|
32 |
2.3 |
3.0 |
||
|
40 |
2.3 |
3.4 |
||
|
50 |
2.9 |
4.6 |
||
|
63 |
3.6 |
5.8 |
||
|
75 |
4.3 |
6.8 |
||
|
90 |
5.2 |
8.2 |
||
|
110 |
6.3 |
10.0 |
||
|
125 |
7.1 |
11.4 |
||
|
140 |
8.0 |
12.7 |
||
|
160 |
9.1 |
14.6 |
||
|
180 |
31.9 |
50.9 |
||
|
200 |
11.4 |
18.2 |
||
|
225 |
12.8 |
20.5 |
||
|
250 |
14.2 |
22.7 |
||
|
315 |
17.9 |
28.6 |
||
|
400 |
22.8 |
36.4 |
||
|
450 |
25.6 |
40.9 |
||
|
500 |
28.4 |
45.5 |
||
|
560 |
31.9 |
50.9 |
||
|
630 |
35.8 |
57.3 |
||
产品用途
物理特性
|
序号 |
项目 |
性能要求 |
试验标准 |
|
|
1 |
长期静液压强度，Mpa(20℃,50年，95%) |
8.0 |
GB15558.1-2003 |
|
|
2 |
短期静液压强度 Mpa |
20℃ |
韧性破坏时间 9.0 (h) ≧100 |
|
|
80℃ |
脆性破坏时间 4.5 (h) ≧165 |
|||
|
破坏时间 4.0 (h) ≧1000 |
||||
|
3 |
热稳定性(200℃),min |
>20 |
||
|
4 |
耐应力开裂，h(80℃,4Mpa) |
≧1000 |
||
|
≧170 |
||||
|
5 |
压缩复原，h(80℃,4Mpa) |
>170 |
||
|
6 |
纵向回缩率(110℃)，% |
≦3 |
||
|
7 |
断裂伸长率 % |
≧350 |
||
|
8 |
耐候性(管材积累受≧3.5KMJ/㎡老化能量后) |
仍能满足本表第2、3、7项性能要求，并保持良好焊接性能 |
||
|
注：适用于工作温度在-20℃-40℃，最大工作压力≦0.7 Mpa的天燃气人工煤气和液化石油气。 |
||||
化学特性
|
介质
|
浓度
|
PE
|
介质
|
浓度
|
PE
|
||
|
200C
|
60C
|
200C
|
60C
|
||||
|
盐酸
|
10%
|
S
|
S
|
高锰酸钾
|
20%
|
S
|
S
|
|
浓缩
|
S
|
S
|
次氯酸钾
|
非饱合
|
S
|
S
|
|
|
硫酸
|
10%
|
S
|
S
|
次氯酸钾
|
15%
|
S
|
S
|
|
50%
|
S
|
S
|
氧化铁（II）（III）
|
饱合
|
S
|
S
|
|
|
98%
|
S
|
N
|
饱合
|
S
|
S
|
||
|
雾
|
NS
|
NS
|
溴（液态）
|
100%
|
NS
|
NS
|
|
|
硝酸
|
25%
|
S
|
S
|
海水
|
|
S
|
S
|
|
50%
|
L
|
NS
|
牛奶
|
|
S
|
S
|
|
|
75%
|
NS
|
NS
|
甲醛
|
40%
|
S
|
S
|
|
|
100%
|
NS
|
NS
|
甲苯
|
100%
|
L
|
NS
|
|
|
氢溴酸
|
50%
|
S
|
S
|
尿不
|
|
S
|
S
|
|
100%
|
S
|
S
|
酸
|
|
S
|
S
|
|
|
乙酸
|
10%
|
S
|
S
|
丁烷（气）
|
100%
|
|
S
|
|
水扬酸
|
饱合
|
S
|
S
|
啤酒
|
|
S
|
S
|
|
甲酸
|
50%
|
S
|
S
|
四氧化碳
|
100%
|
L
|
NS
|
|
98-100%
|
S
|
S
|
甲醇
|
100%
|
S
|
S
|
|
|
苯甲酸
|
非饱合
|
S
|
S
|
葡萄糖
|
饱合
|
S
|
S
|
|
氟硅酸
|
40%
|
S
|
S
|
矿物油
|
|
S
|
L
|
|
铬酸
|
20%
|
S
|
L
|
汽油、石油（脂肪族碳氧化合物）
|
100%
|
S
|
L
|
其他规格